LNP™ LUBRICOMP™ Compound DL0049EF
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP LUBRICOMP DL0049EF compound is based on Polycarbonate (PC) resin containing 20% PTFE, Flame Retardant. Added features of this grade include: Wear Resistant, Flame Retardant, Good Flow.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- PTFE
- Flexural Modulus
- 2060.0 - 2060.0 MPa
- Additives Included
- Flame Retardant, Lubricant (PTFE)
- Flame Retardant
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Material Features
- Easy To Mold
- Flame Retardant
- Friction Resistant
- Good Moldability
- Good Processability
- UL Listed
- Unreinforced
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 47 | MPa | ASTM D638 |
| Tensile Stress (Yield) ¹¹ | 49 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 43 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 40 | MPa | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 5.2 | % | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 5.4 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 23.2 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 26.1 | % | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2060 | MPa | ASTM D638 |
| Flexural Modulus ¹¹ | 2200 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 2060 | MPa | ASTM D790 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2090 | MPa | ISO 527 |
Table 2 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.35 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.35 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.5 - 0.7 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.61 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.8 - 1 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.85 | % | ISO 294 |
| Wear Factor Washer ¹¹ | 8 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.32 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.19 | — | ASTM D3702 Modified: Manual |
Table 3 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 123 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000076 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000756 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000078 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000792 | 1/°C | ASTM E831 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 136 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 126 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Table 4 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1569 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 122 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 32 | J | ASTM D3763 |
| Multi-Axial Impact ¹¹ | 26 | J | ISO 6603 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 118 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 300 - 315 | °C |
| Front - Zone 3 Temperature ⁷ | 310 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 305 - 315 | °C |
| Rear - Zone 1 Temperature ⁷ | 295 - 305 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |