LNP™ LUBRICOMP™ Compound KI001XXJ
LNP LUBRICOMP KI001XXJ compound is based on POM (Acetal) resin containing silicone. Added features of this grade include: Wear Resistant, Healthcare, Food Contact compliant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Pipes & Plumbing
- Consumer Electronics
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Food & Beverage Packaging
- Healthcare Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
- Polyacetals
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyacetal Copolymer (POM)
- Fillers Included
- Silicone, Silicone Oil
- Silicone
- Silicone Oil
- Additives Included
- Lubricant (Silicone)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- Friction Resistant
- Low Extractables
- Low Leachable
- Lubricated
- Unreinforced
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Consumer Applications
- Food Packaging
- Home Appliances
- Hoses
- Medical Devices
- Medical Packaging
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 55 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 52 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 16 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 46 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2750 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 74 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2280 | MPa | ASTM D790 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.24 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 2.4 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 2.4 | % | ASTM D955 |
| Wear Factor Washer ¹¹ | 22 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.44 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.34 | — | ASTM D3702 Modified: Manual |
| Density ¹¹ | 1.4 | g/cm³ | ISO 1183 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 106 | °C | ASTM D648 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1550 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 81 | J/m | ASTM D256 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 200 - 215 | °C |
| Front - Zone 3 Temperature ⁷ | 210 - 220 | °C |
| Middle - Zone 2 Temperature ⁷ | 195 - 205 | °C |
| Rear - Zone 1 Temperature ⁷ | 175 - 190 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |