LNP™ LUBRICOMP™ Compound DFL44

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP LUBRICOMP DFL44 compound is based on Polycarbonate (PC) resin containing 20% glass fiber and 20% PTFE. Added features of this grade include: Internally Lubricated, Wear Resistant.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays
Lighting

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: Glass Fiber, PTFE
Glass Fiber
PTFE
Flexural Modulus: 4900.0 - 4900.0 MPa
Additives Included: Lubricant (PTFE), Lubricant (Unspecified)
Lubricant (PTFE)
Lubricant (Unspecified)
Processing Methods: Injection Molding
Note: ⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна применяться в качестве спецификации или использоваться для проектирования деталей или пресс-форм.; ᵖ Рейтинги UL, указанные в техническом паспорте, могут не охватывать весь диапазон толщин и цветов. Для получения подробной информации, пожалуйста, обратитесь к карточке UL Yellow Card.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 V1
Technology: Plastics
Material Features: Friction Resistant
Lubricated
Wear Resistant
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Circuit Protection
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	86	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.3	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6400	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	127	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	4900	MPa	ISO 178

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density ¹¹	1.48	g/cm³	ISO 1183

Table 3 of 6

4 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	2.60E-05	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000076	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	147	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	142	°C	ISO 75/Af

Table 4 of 6

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	30	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	11	kJ/m²	ISO 180/1A

Table 5 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	305 - 325	°C
Front - Zone 3 Temperature ⁷	320 - 330	°C
Middle - Zone 2 Temperature ⁷	310 - 320	°C
Rear - Zone 1 Temperature ⁷	295 - 305	°C
Mold Temperature ⁷	80 - 110	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 60	rpm