LNP™ LUBRICOMP™ Compound RL0049S

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP RL0049S compound is based on Nylon 6/6 resin containing 20% PTFE. Added features of this grade include: Flame Retardant, Heat Stabilized, Wear Resistant.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: PTFE
Flexural Modulus: 3090.0 - 3090.0 MPa
Additives Included: Flame Retardant, Heat Stabilizer, Lubricant (PTFE); Flame Retardant; Heat Stabilizer; Lubricant (PTFE)
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Material Features: Flame Retardant
Friction Resistant
Heat Stabilized
Unreinforced
Wear Resistant
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Circuit Protection
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	46	MPa	ISO 527
Tensile Stress (Break) ¹¹	47	MPa	ASTM D638
Tensile Strain (Break) ¹¹	2.2	%	ASTM D638
Tensile Strain (Break) ¹¹	2	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	3170	MPa	ASTM D638
Flexural Stress ¹¹	78	MPa	ISO 178
Flexural Stress ¹¹	77	MPa	ASTM D790
Flexural Modulus ¹¹	3090	MPa	ASTM D790
Flexural Modulus ¹¹	2970	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	3160	MPa	ISO 527

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.53	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.38	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.5	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.52	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.7	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.67	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.55	%	ISO 62

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	95	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	90	°C	ISO 75/Af

Table 4 of 5

4 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	170	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	21	J/m	ASTM D256
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	10	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	2	kJ/m²	ISO 180/1A