LNP™ LUBRICOMP™ Compound OL004
- Chemical Family
- Polyphenylene Sulfide (PPS)
LNP LUBRICOMP OL004 compound is based on Polyphenylene Sulfide (PPS) - linear resin containing 20% PTFE. Added features of this grade include: Wear Resistant.
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- PTFE
- Flexural Modulus
- 2950.0 - 2950.0 MPa
- Additives Included
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Product Features
- HDT: 154°C
- Excellent chemical resistance
- Low wear and COF
- Material Features
- Chemical Resistant
- Friction Resistant
- Low Coefficient of Friction
- UL Listed
- Unreinforced
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 58 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 58 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 4.6 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 4 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3100 | MPa | ISO 527 |
| Flexural Strength (at 2 mm/min) ¹¹ | 97 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2950 | MPa | ISO 178 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 53 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 53 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 3 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 3 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 3000 | MPa | ASTM D638 |
Table 2 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.45 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.45 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.02 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
| Wear Factor Washer ¹¹ | 84 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring ¹¹ | 0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.21 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.08 | — | ASTM D3702 Modified: Manual |
Table 3 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 102 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 179 | °C | ISO 75/Bf |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000052 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000053 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 129 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 99 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Table 4 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 20 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 348 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 32 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 2 | J | ASTM D3763 |
Table 5 of 6
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 315 - 320 | °C |
| Front - Zone 3 Temperature ⁷ | 330 - 345 | °C |
| Middle - Zone 2 Temperature ⁷ | 320 - 330 | °C |
| Rear - Zone 1 Temperature ⁷ | 305 - 315 | °C |
| Mold Temperature ⁷ | 140 - 165 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | 1.6 | mm | UL 94 |