LNP™ LUBRICOMP™ Compound MFL36S
- Chemical Family
- PolyolefinsPolypropylenes (PP)
SABIC's Specialties Business LNP LUBRICOMP MFL36S compound is based on Polypropylene (PP) resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Heat Stabilized, Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Aftermarket Parts & Components
- Cooling & Climate
- Equipment & Parts
- Artificial Turf
- Consumer Electronics
- Displays
- Lighting
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Polyolefins
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polypropylene (unspecified)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Additives Included
Heat Stabilizer, Lubricant (PTFE), Mold Release Agent; Heat Stabilizer; Lubricant (PTFE); Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Friction Resistant
- Good Mold Release
- Heat Stabilized
- High Stiffness
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Covers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 85 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 71 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.8 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.9 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 6900 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 7600 | MPa | ASTM D638 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 123 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 117 | MPa | ASTM D790 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 6400 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 5870 | MPa | ASTM D790 |
Table 2 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.26 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.27 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 | % | ASTM D955 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.04 | % | ISO 62-1 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00003 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00000117 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 157 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 140 | °C | ISO 75/Af |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -40°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 40 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -40°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 590 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 90 | J/m | ASTM D256 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 225 - 250 | °C |
| Front - Zone 3 Temperature ⁷ | 240 - 250 | °C |
| Middle - Zone 2 Temperature ⁷ | 215 - 225 | °C |
| Rear - Zone 1 Temperature ⁷ | 195 - 205 | °C |
| Mold Temperature ⁷ | 30 - 50 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |