LNP™ LUBRICOMP™ Compound LX91475
- Chemical Family
- Polyether Ether Ketone (PEEK)
SABIC's Specialties Business LNP LUBRICOMP LX91475 compound is based on Polyetheretherketone (PEEK) resin containing proprietary fillers. Added features of this grade include: Easy Molding, High Temperature Bearing Grade, Wear Resistant.
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyetheretherketone (PEEK)
- Fillers Included
Carbon Fiber, Carbon/Graphite/PTFE, Graphite, PTFE, Proprietary; Carbon Fiber; Carbon/Graphite/PTFE; Graphite; PTFE; Proprietary
- Flexural Modulus
- 10320.0 - 10320.0 MPa
- Additives Included
- Lubricant (Unspecified), Proprietary
- Lubricant (Unspecified)
- Proprietary
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Product Features
- FM: 10.3 GPa
- HDT: 335°C
- Chemical resistance
- Superior bearing performance
- UL94-V0@0.720mm
- Material Features
- Bearing Grade
- Chemical Resistant
- Dimensional Stability
- Easy To Mold
- Friction Resistant
- Good Moldability
- Good Processability
- High Temperature Application
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Bearings
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 6
24 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 139 | MPa | ASTM D638 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 148 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 161 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2 | % | ASTM D638 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 160 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 148 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 159 | MPa | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 11030 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.1 | % | ASTM D638 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2.8 | % | ISO 527 |
| Flexural Stress ¹¹ | 206 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 229 | MPa | ISO 178 |
Table 2 of 6
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.43 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.43 | g/cm³ | ASTM D792 |
| Wear Factor Washer ¹¹ | 16 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Washer ¹¹ | 12 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Washer ¹¹ | 10 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Instr. |
| Dynamic COF ¹¹ | 0.35 | — | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.28 | — | ASTM D3702 Modified: Instr. |
| Static COF ¹¹ | 0.23 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.42 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.56 | — | ASTM D3702 Modified: Instr. |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.1 - 0.2 | % | SABIC method |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.09 | % | ISO 62-1 |
Table 3 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 290 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 322 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000044 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000048 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | min. 300 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 335 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | min. 300 | °C | ISO 75/Af |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 335 | °C | ISO 75/Af |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 336 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000018 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000042 | 1/°C | ASTM D696 |
Table 4 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 480 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 58 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 40 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
| Multi-Axial Impact ¹¹ | 2 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 7 | J | ASTM D3763 |
Table 5 of 6
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Front - Zone 3 Temperature ⁷ | 380 - 400 | °C |
| Middle - Zone 2 Temperature ⁷ | 380 - 400 | °C |
| Rear - Zone 1 Temperature ⁷ | 370 - 380 | °C |
| Mold Temperature ⁷ | 175 - 190 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 60 - 100 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | 0.72 | mm | UL 94 |