LNP™ LUBRICOMP™ Compound DFL36E
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP LUBRICOMP DFL36E compound is based on Polycarbonate (PC) resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Easy Molding, Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 8100.0 - 8100.0 MPa
- Additives Included
- Lubricant (PTFE), Mold Release Agent
- Lubricant (PTFE)
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V1
- Technology
- Plastics
- Material Features
- Easy To Mold
- Friction Resistant
- Good Mold Release
- Good Moldability
- Good Processability
- High Stiffness
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.55 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.57 | g/cm³ | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.11 | % | ISO 62-1 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.6 | % | ASTM D955 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.16 | % | SABIC method |
Table 2 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 1 mm/min) ¹¹ | 8400 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 118 | MPa | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 8100 | MPa | ISO 178 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 123 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.4 | % | ASTM D638 |
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 188 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 9370 | MPa | ASTM D790 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 138 | °C | ISO 75/Af |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00002 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, at 23°C) ¹¹ | 149 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 694 | J/m | ASTM D4812 |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 305 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 320 - 330 | °C |
| Middle - Zone 2 Temperature ⁷ | 310 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 295 - 305 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-1 Flame Class Rating) ᵖ | 3 | mm | UL 94 |