LNP™ LUBRICOMP™ Compound FL004
- Chemical Family
- PolyethylenesPolyolefins
LNP LUBRICOMP FL004 compound is based on Polyethylene (PE) resin containing 20% PTFE. Added features of this grade include: Wear Resistant.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Switches & Relays
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyethylene (unspecified)
- Fillers Included
- PTFE
- Additives Included
- Lubricant (PTFE), Mold Release Agent
- Lubricant (PTFE)
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Friction Resistant
- Good Mold Release
- Unreinforced
- Wear Resistant
- Plastics and Elastomers End Uses
- Air Cabin Interior
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
23 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 25 | MPa | ASTM D638 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 21 | MPa | ISO 527 |
| Tensile Strain (Break) ¹¹ | 42 | % | ASTM D638 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 8.3 | % | ISO 527 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 23 | MPa | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 900 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 1000 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 1430 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 1.20E+01 | MPa | ASTM D638 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 21 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 20 | MPa | ASTM D790 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 800 | MPa | ISO 178 |
Table 2 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.07 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.08 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 2 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 3 - 5 | % | ASTM D955 |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 2.4 - 2.8 | % | SABIC method |
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
| Wear Factor Washer ¹¹ | 9 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring ¹¹ | -1 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.17 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.11 | — | ASTM D3702 Modified: Manual |
Table 3 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 53 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 46 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000152 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000174 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 47 | °C | ISO 75/Af |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 59 | °C | ISO 75/Af |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 74 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000121 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000137 | 1/°C | ASTM D696 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 82 | °C | ISO 75/Bf |
Table 4 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 26 | J/m | ASTM D256 |
| Izod Impact (Notched, at 23°C) ¹¹ | 37 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 100 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1030 | J/m | ASTM D4812 |
| Multi-Axial Impact ¹¹ | 7 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 13 | J | ASTM D3763 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Melt Temperature ⁷ | 230 | °C |
| Front - Zone 3 Temperature ⁷ | 220 - 230 | °C |
| Middle - Zone 2 Temperature ⁷ | 210 - 220 | °C |
| Rear - Zone 1 Temperature ⁷ | 195 - 205 | °C |
| Mold Temperature ⁷ | 40 - 55 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |