LNP™ LUBRICOMP™ Compound WR5210R

Chemical Family: Polycarbonate (PC)

LNP LUBRICOMP WR5210R compound is based on Polycarbonate (PC) resin containing 7% PTFE. Added features of this grade include: Internally Lubricated, Wear Resistant.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays
Lighting

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: PTFE
Additives Included: Impact Modifier, Lubricant (PTFE), Lubricant (Unspecified), Mold Release Agent; Impact Modifier; Lubricant (PTFE); Lubricant (Unspecified); Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 HB
Technology: Plastics
Material Features: Friction Resistant
Good Mold Release
Impact Modified
Lubricated
Unreinforced
Wear Resistant
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 8

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	5.30E+01	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	55	MPa	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	75	%	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	83	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2030	MPa	ASTM D790

Table 2 of 8

2 rows

Characteristic	Value	Unit	Method
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.4 - 0.6	%	SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	21.5	g/10 min	ASTM D1238

Table 3 of 8

4 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	126	°C	ASTM D648
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Table 4 of 8

5 rows

Characteristic	Value	Unit	Method
High Voltage Arc Track Rate (PLC) ¹¹	2	PLC Code	UL 746A
Comparative Tracking Index (UL, PLC) ¹¹	3	PLC Code	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 3	mm	UL 746A
Hot Wire Ignition (PLC 3) ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 1.5	mm	UL 746A

Table 5 of 8

1 row

Characteristic	Value	Method
Gloss (Untextured, 60°) ¹¹	52	ASTM D523

Table 6 of 8