LNP™ LUBRICOMP™ Compound RFL36L
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP LUBRICOMP RFL36L compound is based on Nylon 6/6 resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Low Extractable.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Powertrain & UTH
Building & Construction — Building Materials
- Pipes & Plumbing
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Healthcare & Pharma — Medical
- Medical Devices & Assemblies
Printing & Packaging — Packaging
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 8270.0 - 8270.0 MPa
- Additives Included
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- Friction Resistant
- High Stiffness
- Low Extractables
- Low Leachable
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Automotive Gears
- Building Materials
- Consumer Applications
- Food Packaging
- Home Appliances
- Hoses
- Medical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 152 | MPa | ISO 527 |
| Tensile Stress (Yield) ¹¹ | 151 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 152 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 151 | MPa | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 2.8 | % | ISO 527 |
| Tensile Strain (Yield) ¹¹ | 2.8 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.8 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.8 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 10050 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 230 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 213 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 9300 | MPa | ISO 178 |
Table 2 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.52 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.52 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.53 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.3 - 1.5 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.4 | % | ISO 294 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.4 | % | ASTM D570 |
| Wear Factor Washer ¹¹ | 4 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.66 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.65 | — | ASTM D3702 Modified: Manual |
Table 3 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 260 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 247 | °C | ISO 75/Af |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000288 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000029 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000738 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000074 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 261 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 252 | °C | ASTM D648 |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 61 | kJ/m² | ISO 180/1U |
| Multi-Axial Impact ¹¹ | 2 | J | ISO 6603 |
| Izod Impact (Notched, at 23°C) ¹¹ | 96 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1009 | J/m | ASTM D4812 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 12 | J | ASTM D3763 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 265 - 275 | °C |
| Mold Temperature ⁷ | 95 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |