To catalogue
LNP™ LUBRICOMP™ Compound WFL28
- Chemical Family
- Polyesters
SABIC's Specialties Business LNP LUBRICOMP WFL28 compound is based on Polybutylene Terephthalate (PBT) resin containing 40% glass fiber, 10% PTFE. Added features of this grade include: Internally Lubricated, Wear Resistant.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 10800.0 - 10800.0 MPa
- Additives Included
- Lubricant (PTFE), Lubricant (Unspecified)
- Lubricant (PTFE)
- Lubricant (Unspecified)
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Friction Resistant
- High Stiffness
- Lubricated
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Covers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 126 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.3 | % | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 187 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 10800 | MPa | ISO 178 |
Table 2 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.7 | g/cm³ | ISO 1183 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
Table 4 of 4
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 | % |
| Melt Temperature ⁷ | 240 - 265 | °C |
| Front - Zone 3 Temperature ⁷ | 260 - 270 | °C |
| Middle - Zone 2 Temperature ⁷ | 245 - 255 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 230 | °C |
| Mold Temperature ⁷ | 80 - 100 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |