LNP™ LUBRICOMP™ Compound RFN18SXS

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP RFN18SXS compound is based on Nylon 6/6 resin containing 40% glass fiber, Molybdenum diSulfide (MoS2). Added features of this grade include: Heat Stabilized, Wear Resistant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Glass Fiber, Molybdenum Disulfide
Glass Fiber
Molybdenum Disulfide
Flexural Modulus: 11100.0 - 11100.0 MPa
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Friction Resistant
Heat Stabilized
High Stiffness
No Added PFAS
Wear Resistant
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	219	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.8	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	13300	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	311	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	11100	MPa	ISO 178

Table 2 of 5

5 rows

Characteristic	Value	Unit	Method
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.15 - 0.35	%	SABIC method
Wear Factor Washer ¹¹	45	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.75	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.59	—	ASTM D3702 Modified: Manual
Density ¹¹	1.51	g/cm³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	261	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	254	°C	ISO 75/Af

Table 4 of 5