LNP™ LUBRICOMP™ Compound NX20BSR
SABIC's Specialties Business LNP LUBRICOMP NX20BSR compound is based on a low-gloss black Polycarbonate / Acrylonitrile Butadiene Styrene (PC/ABS) blend with good Buzz, Squeak and Rattle (BSR) performance. Added features of this grade include: Low Slip-Stick, Internally Lubricated and Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Electrical & Electronic Systems
- Exterior & Body
- Interior
- Artificial Turf
- Automotive Electronics
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Density
- 1120.0 - 1120.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2090.0 - 2090.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Additives Included
- Lubricant (Unspecified)
- Material Features
- Excellent BSR Performance
- Lubricated
- Unreinforced
- Wear Resistant
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Infotainment
- Automotive Interior Parts
- Automotive Interior Trim
- Back Mirror
- Building Materials
- Cell Phones
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 1 mm/min) ¹¹ | 2170 | MPa | ISO 527 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 50 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 44 | MPa | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 67 | % | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2090 | MPa | ISO 178 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2280 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 56 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 46 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 86 | % | ASTM D638 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2180 | MPa | ASTM D790 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.12 | g/cm³ | ISO 1183 |
| Dynamic COF ¹¹ | 0.33 | — | ASTM D3702 Modified: Manual |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.097 | % | ASTM D570 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.7 - 0.9 | % | SABIC method |
| Mold Shrinkage (xflow) ᵍ ¹¹ | 0.8 - 1 | % | SABIC method |
| Melt Volume Rate (at 260°C, 5.0 kg) ¹¹ | 21 | cm³/10 min | ISO 1133 |
| Melt Flow Rate (at 260°C, 5.0 kgf) ¹¹ | 23 | g/10 min | ASTM D1238 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 104 | °C | ISO 75/Af |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 126 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 124 | °C | ISO 306 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 125 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 103 | °C | ASTM D648 |
Table 4 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 208 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 40 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 248 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 14 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -40°C) ¹¹ | 14 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 402 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 49 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 16 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -40°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 16 | kJ/m² | ISO 179/1eA |
| Izod Impact (Notched, at 23°C) ¹¹ | 747 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 463 | J/m | ASTM D256 |
Table 5 of 5
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 105 - 110 | °C |
| Drying Time (Cumulative) ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 9 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 275 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 260 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 255 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 290 | °C |
| Mold Temperature ⁷ | 60 - 80 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |