LNP™ LUBRICOMP™ Compound UCL16AS

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP UCL16AS compound is based on Polyphthalamide (PPA) resin containing 5% PTFE and 30% carbon fiber. Added features of this grade include: Heat Stabilized, Wear Resistant, Electrically Conductive.

Product families

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyphthalamide (PPA)
Fillers Included: Carbon Fiber, PTFE
Carbon Fiber
PTFE
Flexural Modulus: 19000.0 - 19000.0 MPa
Additives Included: Heat Stabilizer, Lubricant (PTFE), Mold Release Agent; Heat Stabilizer; Lubricant (PTFE); Mold Release Agent
Processing Methods: Injection Molding
Note: ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.. ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Industrial
Technology: Plastics
Material Features: Electrically Conductive
Friction Resistant
Good Mold Release
Heat Stabilized
High Stiffness
High Strength
High Temperature Resistance
Light Weight
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Under The Hood
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	272	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.4	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	21800	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	373	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	19000	MPa	ISO 178

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density ¹¹	1.36	g/cm³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000007	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000046	1/°C	ISO 11359-2

Table 4 of 5