LNP™ LUBRICOMP™ Compound CG006
- Chemical Family
- Styrenics
SABIC's Specialties Business LNP LUBRICOMP CG006 compound is based on Polystyrene (PS) resin containing graphite. Added features of this grade include: Wear Resistant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Glazing & Window Elements
- Interior Fixtures
- Pipes & Plumbing
- Equipment & Parts
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polystyrene (unspecified)
- Fillers Included
- Graphite
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Friction Resistant
- Good Mold Release
- Heat Stabilized
- High Impact Performance
- No Added PFAS
- Wear Resistant
- Plastics and Elastomers End Uses
- Building Materials
- Construction Applications
- Faucet System Components
- Fittings
- Gears
- Hoses
- Housings
- Pipes
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 45 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 6200 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 72 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 5400 | MPa | ISO 178 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 6600 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1.2 | % | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 74 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2100 | MPa | ASTM D790 |
Table 2 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
| Wear Factor Washer ¹¹ | 799 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Instr. |
| Dynamic COF ¹¹ | 0.3 | — | ASTM D3702 Modified: Instr. |
| Static COF ¹¹ | 0.55 | — | ASTM D3702 Modified: Instr. |
| Density ¹¹ | 1.22 | g/cm³ | ISO 1183 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 99 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 101 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 89 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 97 | °C | ISO 75/Bf |
Table 4 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 2 | kJ/m² | ISO 180/1A |
| Charpy Impact (Unnotched, at 23°C) ¹¹ | 6.5 | kJ/m² | ISO 179/2C |
| Charpy Impact (Notched, at 23°C) ¹¹ | 1.2 | kJ/m² | ISO 179/2C |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | 6.5 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 1.2 | kJ/m² | ISO 179/1eA |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 80 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 12 | J/m | ASTM D256 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 250 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 245 - 255 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 230 | °C |
| Mold Temperature ⁷ | 40 - 65 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |