LNP™ LUBRICOMP™ Compound DCI06APW
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP LUBRICOMP DCI06APW compound is based on Polycarbonate (PC) resin containing 30% carbon fiber and silicone. Added features of this grade include: Electrically Conductive, High Flow, Wear Resistant. Healthcare, Biocompatible (ISO10993). This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Tubing & Fluids Handling
- Healthcare Packaging
- Industrial & Transport Packaging
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Carbon Fiber, Silicone
- Carbon Fiber
- Silicone
- Flexural Modulus
- 20600.0 - 20600.0 MPa
- Additives Included
- Lubricant (Silicone), Lubricant (Unspecified)
- Lubricant (Silicone)
- Lubricant (Unspecified)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Biocompatible
- No Added PFAS
- Material Features
- Biocompatible
- Electrically Conductive
- Friction Resistant
- Good Moldability
- Good Processability
- High Flow
- High Modulus
- Light Weight
- Plastics and Elastomers End Uses
- Fluid Handling
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
- Compounds Wear and Friction Solutions Medical Devices
For a medical device, whether it be a drug delivery pen or a laparoscopic surgical tool, repeatable and efficient motion is critical to performance. The friction between moving parts plays a large role in how a device is perceived and accepted by both consumers and healthcare professionals. LUBRICOMP™ and LUBRILOY™ compounds can help deliver the performance required.; Growing List of Demands; The demands on wear and friction materials for medical devices grow as sterilization and cleaning techniques evolve, parts get smaller and thinner, and market trends move towards more consumer friendly styling and colors. Add the heightened emphasis on system cost optimization and the need for innovative internally lubricated thermoplastic solutions expands.; Internally Lubricated Compounds; The addition of an internal lubricant to a thermoplastic material can reduce the coefficient of friction between two plastic parts, allowing them to slide past each other smoothly with minimal wear. Traditional lubricants like medical grade silicone and PTFE can be combined with advanced PC copolymer technology to deliver the required performance in thin wall parts.
Technical data
Table 1 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic COF ¹¹ | 0.24 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.22 | — | ASTM D3702 Modified: Manual |
| Wear Factor Washer ¹¹ | 13 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Specific Gravity ¹¹ | 1.3 | — | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.11 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.05 - 0.15 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.15 - 0.4 | % | ASTM D955 |
| Melt Volume Rate (at 300°C, 5.0 kg) ¹¹ | 28 | cm³/10 min | ASTM D1238 |
Table 2 of 6
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 183 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1.4 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 25440 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 265 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 20100 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 183 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.6 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 23830 | MPa | ISO 527 |
| Flexural Strength (at 2 mm/min) ¹¹ | 262 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 20600 | MPa | ISO 178 |
| Compressive Strength ¹¹ | 128 | MPa | SABIC method |
| Shear Modulus ¹¹ | 3508 | MPa | ASTM D732 |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 128 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.0000097 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000046 | 1/°C | ASTM D696 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 130 | °C | ISO 75/Af |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 1000 | Ω | ASTM D257 |
Table 5 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 504 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 94 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 16 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 33 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
Table 6 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 290 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 285 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 275 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 270 - 285 | °C |
| Mold Temperature ⁷ | 100 - 120 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 40 - 80 | rpm |
| Maximum Moisture Content ⁷ | 0.02 | % |