LNP™ LUBRICOMP™ Compound LCL33EXQ

Chemical Family: Polyether Ether Ketone (PEEK)

SABIC's Specialties Business LNP LUBRICOMP LCL33EXQ compound is based on Polyetheretherketone (PEEK) resin containing 15% carbon fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Easy Molding, Electrically Conductive.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyetheretherketone (PEEK)
Fillers Included: Carbon Fiber, PTFE
Carbon Fiber
PTFE
Flexural Modulus: 13530.0 - 13530.0 MPa
Additives Included: Lubricant (PTFE)
Processing Methods: Injection Molding
Note: ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.. ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Industrial
Personal Care
Printing & Packaging
Technology: Plastics
Material Features: Easy To Mold
Electrically Conductive
Friction Resistant
Good Moldability
Good Processability
High Stiffness
High Strength
High Temperature Application
Plastics and Elastomers End Uses: Appliances
Bearings
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

6 rows

Characteristic	Value	Unit	Method
Melt Flow Rate (at 400°C, 5.0 kgf) ¹¹	32	g/10 min	ASTM D1238
Specific Gravity ¹¹	1.45	—	ASTM D792
Poisson's Ratio ¹¹	0.43	—	ISO 527-1/2
Wear Factor Washer ¹¹	14	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.37	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.35	—	ASTM D3702 Modified: Manual

Table 2 of 5

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	185	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.8	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	16000	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	277	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	13400	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	181	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.6	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	13960	MPa	ISO 527
Flexural Stress ¹¹	276	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	13530	MPa	ISO 178

Table 3 of 5

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	320	°C	ASTM D648

Table 4 of 5

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Notched, at 23°C) ¹¹	69	J/m	ASTM D256
Izod Impact (Notched, 80104, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Table 5 of 5

8 rows

Characteristic	Value	Unit
Drying Temperature ⁷	150	°C
Drying Time ⁷	4 - 6	Hrs
Front - Zone 3 Temperature ⁷	380 - 400	°C
Middle - Zone 2 Temperature ⁷	380 - 400	°C
Rear - Zone 1 Temperature ⁷	370 - 380	°C
Mold Temperature ⁷	175 - 190	°C
Back Pressure ⁷	0.3 - 0.7	MPa
Screw Speed ⁷	60 - 100	rpm