LNP™ LUBRICOMP™ Compound WR2210
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP LUBRICOMP WR2210 compound is based on Polycarbonate (PC) resin containing proprietary lubricant. Added features of this grade include: Internally Lubricated, Wear Resistant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Additives Included
Flame Retardant, Heat Stabilizer, Lubricant (Unspecified), Proprietary; Flame Retardant; Heat Stabilizer; Lubricant (Unspecified); Proprietary
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ¹⁷ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Flame Retardant
- Friction Resistant
- Heat Stabilized
- Lubricated
- No Added PFAS
- Unreinforced
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 5 mm/min) ¹¹ | 2000 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 59 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 94 | % | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 88 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2390 | MPa | ASTM D790 |
| K-factor (xE-10, PV=2000 psi-fpm vs Steel) ¹¹ | 85 | — | SABIC method |
| Coefficient of Friction (on steel, Static) ¹¹ | 0.17 | — | ASTM D1894 |
| Coefficient of Friction (on steel, Kinetic) ¹¹ | 0.21 | — | ASTM D1894 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 18.2 | g/10 min | ASTM D1238 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 15 | cm³/10 min | ISO 1133 |
Table 3 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 127 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 127 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.00007 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 100 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 100 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 100 | °C | UL 746B |
| Thermal Conductivity ¹¹ | 0.2 | W/m-°C | ISO 8302 |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hot Wire Ignition (PLC 2) ¹⁷ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 4) ¹⁷ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹⁷ | min. 3 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹⁷ | min. 1.5 | mm | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹⁷ | 3 | PLC Code | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹⁷ | 2 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹⁷ | 5 | PLC Code | ASTM D495 |
Table 5 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 630 | J/m | ASTM D256 |
| Tensile Impact Strength (Type S) ¹¹ | 630 | kJ/m² | ASTM D1822 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 56 | J | ASTM D3763 |
| Izod Impact (Notched, at -20°C) ¹¹ | 150 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 20 | kJ/m² | ISO 180/1A |
| Charpy Impact (Notched, at 23°C, 80*10*4mm, Cut) ¹¹ | 35 | kJ/m² | ISO 179/1eA |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Nozzle Temperature ⁷ | 275 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |