LNP™ LUBRICOMP™ Compound RA004

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP RA004 compound is based on Nylon 6/6 resin containing 20% aramid fiber. Added features of this grade include: Wear Resistant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Aramid Fiber
Flexural Modulus: 4410.0 - 4410.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Friction Resistant
Good Mold Release
No Added PFAS
Wear Resistant
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

8 rows

Characteristic	Value	Unit	Method
Tensile Strain (Break, 5 mm/min) ¹¹	3.6	%	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	85	MPa	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	4000	MPa	ISO 178
Flexural Stress (Break, 2 mm/min) ¹¹	122	MPa	ISO 178
Tensile Stress (Break) ¹¹	88	MPa	ASTM D638
Tensile Strain (Break) ¹¹	4.5	%	ASTM D638
Flexural Stress ¹¹	137	MPa	ASTM D790
Flexural Modulus ¹¹	4410	MPa	ASTM D790

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.2	g/cm³	ISO 1183
Density ¹¹	1.23	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.5	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	2	%	ASTM D955
Dynamic COF ¹¹	0.52	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.66	—	ASTM D3702 Modified: Manual
Wear Factor Washer ¹¹	59	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual

Table 3 of 5

4 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	199	°C	ISO 75/Af
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.00006	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.00009	1/°C	ISO 11359-2
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	171	°C	ASTM D648

Table 4 of 5