LNP™ LUBRICOMP™ Compound UX05051

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP UX05051 compound is based on Polyphthalamide (PPA) resin containing glass fiber and PTFE. Added features of this grade include: Heat Stabilized, Flame Retardant, Hot Water Moldable, Wear Resistant.

Product families

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Housings & Enclosures
Semiconductor Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyphthalamide (PPA)
Fillers Included: Glass Fiber, PTFE
Glass Fiber
PTFE
Flexural Modulus: 10700.0 - 10700.0 MPa
Additives Included: Flame Retardant, Heat Stabilizer, Lubricant (PTFE), Mold Release Agent; Flame Retardant; Heat Stabilizer; Lubricant (PTFE); Mold Release Agent
Processing Methods: Injection Molding
Note: ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Industrial
Flame Rating: UL 94 V0
Technology: Plastics
Material Features: Flame Retardant
Friction Resistant
Good Mold Release
Heat Stabilized
High Temperature Resistance
Lubricated
Very Good Heat Resistance
Wear Resistant
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Under The Hood
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	138	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	12100	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	188	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	10700	MPa	ISO 178

Table 2 of 7

1 row

Characteristic	Value	Unit	Method
Density ¹¹	1.76	g/cm³	ISO 1183

Table 3 of 7

6 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.00002	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000052	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	273	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	140	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	140	°C	UL 746B

Table 4 of 7

3 rows

Characteristic	Value	Unit	Method
Comparative Tracking Index (UL, PLC) ¹¹	1	PLC Code	UL 746A
Hot Wire Ignition (PLC 0) ¹¹	min. 0.4	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 0.8	mm	UL 746A

Table 5 of 7

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	25	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	8	kJ/m²	ISO 180/1A

Table 6 of 7

9 rows

Characteristic	Value	Unit
Drying Temperature ⁷	80	°C
Drying Time ⁷	4	Hrs
Melt Temperature ⁷	305 - 315	°C
Front - Zone 3 Temperature ⁷	305 - 320	°C
Middle - Zone 2 Temperature ⁷	305 - 320	°C
Rear - Zone 1 Temperature ⁷	305 - 320	°C
Mold Temperature ⁷	95 - 120	°C
Back Pressure ⁷	0.3 - 0.7	MPa
Screw Speed ⁷	30 - 60	rpm

Table 7 of 7