LNP™ LUBRICOMP™ Compound KA000M
SABIC's Specialties Business LNP LUBRICOMP KA000M compound is based on POM (Acetal) resin containing aramid powder and proprietary lubricant. Added features of this grade include: Internally Lubricated, Wear Resistant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- Polyacetals
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyacetal Copolymer (POM)
- Fillers Included
- Aramid Fiber, Aramid Powder
- Aramid Fiber
- Aramid Powder
- Flexural Modulus
- 2400.0 - 2400.0 MPa
- Additives Included
- Lubricant (Unspecified), Proprietary
- Lubricant (Unspecified)
- Proprietary
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Dimensional Stability
- Friction Resistant
- Low Slip
- Low Wear
- Lubricated
- No Added PFAS
- Vibration Damping
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.2 - 0.3 | % | ASTM D570 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.2 - 0.4 | % | ASTM D570 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.2 - 0.4 | % | ISO 62-1 |
| Dynamic COF ¹¹ | 0.2 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.22 | — | ASTM D3702 Modified: Manual |
| Wear Factor Washer ¹¹ | 9 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.2 - 0.3 | % | ISO 62 |
| Melt Volume Rate (at 190°C, 2.16 kg) ¹¹ | 4 - 6 | cm³/10 min | ISO 1133 |
| Density ¹¹ | 1.35 | g/cm³ | ISO 1183 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 1.5 - 2.5 | % | SABIC method |
| Mold Shrinkage (xflow) ᵍ ¹¹ | 1.5 - 2.5 | % | SABIC method |
Table 2 of 6
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 5 mm/min) ¹¹ | 2600 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 5.3 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 6 | % | ASTM D638 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 42 | MPa | ASTM D638 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2600 | MPa | ASTM D790 |
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 74 | MPa | ASTM D790 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2400 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min, 60°C) ¹¹ | 1400 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min, 100°C) ¹¹ | 800 | MPa | ISO 178 |
| Flexural Strain (Break, at 2 mm/min) ¹¹ | 7 | % | ISO 178 |
| Flexural Strain (Break, at 2 mm/min, 60°C) ¹¹ | 7 | % | ISO 178 |
| Flexural Strain (Break, at 2 mm/min, 100°C) ¹¹ | 7 | % | ISO 178 |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 96 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 143 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 143 | °C | ISO 306 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00012 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00013 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 90 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 150 | °C | ISO 75/Bf |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 144 | °C | ISO 306 |
Table 4 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 28 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 310 | J/m | ASTM D4812 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 2 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 30 | kJ/m² | ISO 179/1eU |
Table 5 of 6
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 200 - 215 | °C |
| Rear - Zone 1 Temperature ⁷ | 175 - 190 | °C |
| Middle - Zone 2 Temperature ⁷ | 195 - 205 | °C |
| Front - Zone 3 Temperature ⁷ | 210 - 220 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |