LNP™ LUBRICOMP™ Compound RFL369

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRICOMP RFL369 compound is based on Nylon 6/6 resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Flame Retardant, Wear Resistant.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Powertrain & UTH

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRICOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Glass Fiber, PTFE
Glass Fiber
PTFE
Flexural Modulus: 8500.0 - 8500.0 MPa
Additives Included: Flame Retardant, Lubricant (PTFE), Mold Release Agent; Flame Retardant; Lubricant (PTFE); Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 V0
Technology: Plastics
Material Features: Flame Retardant
Friction Resistant
Good Mold Release
High Stiffness
UL Listed
Wear Resistant
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Automotive Gears
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

6 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, 5 mm/min) ¹¹	128	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	11500	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	152	MPa	ISO 178
Flexural Strain (Break, at 2 mm/min) ¹¹	2.5	%	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	8500	MPa	ISO 178

Table 2 of 7

2 rows

Characteristic	Value	Unit	Method
Mold Shrinkage (flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Density ¹¹	1.74	g/cm³	ISO 1183

Table 3 of 7

4 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000042	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000078	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	253	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	225	°C	ISO 75/Af

Table 4 of 7

1 row

Characteristic	Value	Unit	Method
Comparative Tracking Index ¹¹	375	V	IEC 60112

Table 5 of 7