LNP™ STAT-KON™ Compound RE0039

Chemical Family: Polyamides

LNP STAT-KON RE0039 compound is based on Nylon 6/6 resin containing 15% carbon fiber. Added features of this grade include: Electrically Conductive, Flame Retardant.

Product families

Applications

Consumer Goods — Cold-Chain & Insulation

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ STAT-KON™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Carbon Fiber
Flexural Modulus: 11440.0 - 11440.0 MPa
Additives Included: Flame Retardant, Mold Release Agent
Flame Retardant
Mold Release Agent
Processing Methods: Injection Molding
Note: ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.; ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Consumer Goods
Electrical & Electronics
Industrial
Flame Rating: UL 94 5VA
UL 94 V0
Technology: Plastics
Material Features: Electrically Conductive
Flame Retardant
Good Mold Release
High Stiffness
High Strength
Light Weight
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Computer Components
Electrical/Electronic Applications
Electronic Components
Freezer
Industrial Applications
Semiconductor Applications
Wiring Devices
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	205	MPa	ASTM D638
Tensile Stress (Break) ¹¹	209	MPa	ISO 527
Tensile Strain (Break) ¹¹	2.2	%	ASTM D638
Tensile Strain (Break) ¹¹	2.2	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	17580	MPa	ASTM D638
Flexural Stress ¹¹	297	MPa	ASTM D790
Flexural Stress ¹¹	318	MPa	ISO 178
Flexural Modulus ¹¹	11440	MPa	ASTM D790
Flexural Modulus ¹¹	14200	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	15600	MPa	ISO 527

Table 2 of 7

7 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.44	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.55	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2 - 0.3	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.17 - 0.26	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 0.8	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.68 - 0.78	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.87	%	ISO 62

Table 3 of 7

9 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	247	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000457	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000457	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000066	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000661	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	228	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	65	°C	UL 746B

Table 4 of 7

1 row

Characteristic	Value	Unit	Method
Surface Resistivity ᵈ ¹¹	100 - 1000000	Ω	ASTM D257

Table 5 of 7

6 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	704	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	74	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	8	J	ASTM D3763
Multi-Axial Impact ¹¹	2	J	ISO 6603
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	46	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	8	kJ/m²	ISO 180/1A

Table 6 of 7