LEXAN™ VISUALFX™ Resin FXEMPX1L
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business Opaque EXL, UV-Stabilized & light shielding capability, for portable electronics device enclosure application. Only available in white, gray and limited pastel colors. Consult CIC or PM for color availability & limitation.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Consumer Electronics
- Displays
- Advanced Materials
- Off Road & Recreational Vehicle (RV)
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LEXAN™ VISUALFX™ Resin
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Titanium Dioxide
- Additives Included
Heat Stabilizer, Mold Release Agent, UV Stabilizer; Heat Stabilizer; Mold Release Agent; UV Stabilizer
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовая инжекция.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Color
- Opaque
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Material Features
- Good Aesthetics
- Good Mold Release
- Good Surface Appearance
- Heat Stabilized
- High Impact Performance
- High Impact Resistance
- UV Stabilized
- Unreinforced
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Displays
- Electrical/Electronic Applications
- Enclosure
- Home Appliances
- Military Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 51 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 46 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 66 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2040 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 80 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 1990 | MPa | ASTM D790 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.3 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 15 | cm³/10 min | ISO 1133 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 114 | °C | ASTM D648 |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 530 | J/m | ASTM D256 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 295 - 315 | °C |
| Nozzle Temperature ⁷ | 290 - 310 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 305 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |