LNP™ LUBRILOY™ Compound RF206AXH

Chemical Family: Polyamides

SABIC's Specialties Business LNP LUBRILOY RF206AXH compound is based on Nylon 6/6 resin containing 30% glass fiber and proprietary lubricant. Added features of this grade include: Wear Resistant, Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies
Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging
Industrial & Transport Packaging

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ LUBRILOY™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Glass Fiber
Flexural Modulus: 7200.0 - 7200.0 MPa
Additives Included: Heat Stabilizer, Lubricant (Unspecified), Mold Release Agent, Proprietary; Heat Stabilizer; Lubricant (Unspecified); Mold Release Agent; Proprietary
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Friction Resistant
Good Mold Release
Heat Stabilized
Lubricated
No Added PFAS
Wear Resistant
Plastics and Elastomers End Uses: Medical Devices
Medical Packaging
Medical/Healthcare Applications
Pharmaceutical Packaging
Surgical Devices
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	121	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.5	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	8760	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	173	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	7060	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	118	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.3	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	8460	MPa	ISO 527
Flexural Stress ¹¹	167	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7200	MPa	ISO 178

Table 2 of 5

8 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.24	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.38	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.6	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.2	%	ASTM D955
Wear Factor Washer ¹¹	45	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.4	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.4	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.66	%	ISO 62

Table 3 of 5

6 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	258	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	241	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000038	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000075	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	252	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	224	°C	ISO 75/Af

Table 4 of 5