LNP™ LUBRILOY™ Compound UA200A
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP LUBRILOY UA200A compound is based on Polyphthalamide (PPA) resin containing aramid fiber and proprietary lubricant. Added features of this grade include: Wear Resistant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Exterior & Body
- Powertrain & UTH
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ LUBRILOY™ Compound
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Aramid Fiber
- Flexural Modulus
- 3720.0 - 3720.0 MPa
- Additives Included
Heat Stabilizer, Lubricant (Unspecified), Mold Release Agent, Proprietary; Heat Stabilizer; Lubricant (Unspecified); Mold Release Agent; Proprietary
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Friction Resistant
- Good Mold Release
- Heat Stabilized
- High Temperature Resistance
- Lubricated
- No Added PFAS
- Non-Halogenated
- Very Good Heat Resistance
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Under The Hood
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 86 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 3.3 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 4290 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 131 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 3720 | MPa | ASTM D790 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.16 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.42 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.9 - 1.1 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.4 - 1.6 | % | ASTM D955 |
| Wear Factor Washer ¹¹ | 5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.25 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.21 | — | ASTM D3702 Modified: Manual |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 253 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 118 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000045 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000593 | 1/°C | ASTM E831 |
| Thermal Conductivity ¹¹ | 0.29 | W/m-°C | ASTM E1530 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 603 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 32 | J/m | ASTM D256 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 | % |
| Melt Temperature ⁷ | 310 - 315 | °C |
| Front - Zone 3 Temperature ⁷ | 305 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 305 - 315 | °C |
| Rear - Zone 1 Temperature ⁷ | 305 - 315 | °C |
| Mold Temperature ⁷ | 120 - 150 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |