To catalogue
LNP™ LUBRILOY™ Compound RF203XXH
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP™ LUBRILOY™ RF203XXH compound is based on Nylon 6/6 resin containing 15% glass fiber and proprietary lubricant. Added features of this grade include: Wear Resistant, Healthcare.
Product families
Applications
Healthcare & Pharma — Medical
- Medical Devices & Assemblies
- Surgical Instruments & Trays
Printing & Packaging — Packaging
- Healthcare Packaging
- Industrial & Transport Packaging
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- LNP™ LUBRILOY™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 5500.0 - 5500.0 MPa
- Additives Included
- Lubricant (Unspecified), Proprietary
- Lubricant (Unspecified)
- Proprietary
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Lubricated
- Wear Resistant
- Plastics and Elastomers End Uses
- Electronic Components
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 87 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 3.7 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 4890 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 128 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 4180 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 90 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3.8 | % | ISO 527 |
| Flexural Stress ¹¹ | 140 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 5500 | MPa | ISO 178 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.12 | — | ASTM D792 |
| Density ¹¹ | 1.13 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.13 | g/cm³ | ISO 1183 |
| Wear Factor Washer ¹¹ | 70 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.36 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.3 | — | ASTM D3702 Modified: Manual |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ⁷ | 232 | °C | ISO 75/Af |
Table 4 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 646 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 83 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 270 - 280 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 265 - 275 | °C |
| Mold Temperature ⁷ | 80 - 95 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |