LNP™ THERMOCOMP™ Compound LX97024

Chemical Family: Polyether Ether Ketone (PEEK)

SABIC's Specialties Business LNP™ THERMOCOMP™ LX97024 compound is based on Polyetheretherketone (PEEK) resin containing 15% glass fiber, 5% PTFE. Added features of this grade include: Internally Lubricated, Easy Molding.

Product families

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays
Industrial Automation

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Semiconductor Manufacturing
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyetheretherketone (PEEK)
Fillers Included: Glass Fiber, PTFE
Glass Fiber
PTFE
Flexural Modulus: 6000.0 - 6000.0 MPa
Additives Included: Lubricant (PTFE), Lubricant (Unspecified)
Lubricant (PTFE)
Lubricant (Unspecified)
Processing Methods: Injection Molding
Note: ⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые размеры литья, литье крупных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.; ᵖ Рейтинги UL, указанные в техническом паспорте, могут не охватывать весь диапазон толщин и цветов. Для получения подробной информации, пожалуйста, обратитесь к карточке UL Yellow Card.
Markets: Consumer Goods
Electrical & Electronics
Industrial
Flame Rating: UL 94 V0
Technology: Plastics
Material Features: Cost Effective
Easy To Mold
Friction Resistant
Good Moldability
Good Processability
High Modulus
High Stiffness
High Temperature Resistance
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Displays
Electrical Components
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	114	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.3	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6900	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	177	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	6000	MPa	ISO 178

Table 2 of 7

1 row

Characteristic	Value	Unit	Method
Density ¹¹	1.41	g/cm³	ISO 1183

Table 3 of 7

3 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000027	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.00005	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	280	°C	ISO 75/Af

Table 4 of 7

4 rows

Characteristic	Value	Unit	Method
Comparative Tracking Index (UL, PLC) ¹¹	4	PLC Code	UL 746A
Hot Wire Ignition (PLC 0) ¹¹	min. 3	mm	UL 746A
Hot Wire Ignition (PLC 1) ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 4) ¹¹	min. 1.5	mm	UL 746A

Table 5 of 7

2 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	30	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Table 6 of 7

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120 - 150	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.1	%
Melt Temperature ⁷	380 - 390	°C
Front - Zone 3 Temperature ⁷	380 - 395	°C
Middle - Zone 2 Temperature ⁷	365 - 375	°C
Rear - Zone 1 Temperature ⁷	350 - 360	°C
Mold Temperature ⁷	140 - 165	°C
Back Pressure ⁷	0.3 - 0.7	MPa
Screw Speed ⁷	60 - 100	rpm

Table 7 of 7