LNP THERMOCOMP KF004AL compound is based on Acetal (POM) Homopolymer resin containing 20% glass fiber. Added features of this grade include: Low Extractables.
Product families
Applications
Applications
Consumer Goods — Appliances & Electronics
Building & Construction — Building Materials
Pipes & Plumbing
Electrical & Electronics — Devices & Assemblies
Consumer Electronics
Printing & Packaging — Packaging
Food & Beverage Packaging
Industrial & Transport Packaging
Non-Food Consumer Packaging
Electrical & Electronics — Parts & Components
Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
Polyacetals
Other characteristics
Brand
LNP™ THERMOCOMP™ Compound
Polymer Name
Polyacetal Homopolymer (POM)
Fillers Included
Glass Fiber
Flexural Modulus
7580.0 - 7580.0 MPa
Processing Methods
Injection Molding
Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets
Building & Construction
Consumer Goods
Electrical & Electronics
Printing & Packaging
Technology
Plastics
Labeling Claims
Food Contact Acceptable
Material Features
Cost Effective
Food Contact Acceptable
High Impact Resistance
High Modulus
High Stiffness
Low Extractables
Low Leachable
Country Availability
Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses
Appliances
Building Materials
Consumer Applications
Electrical Enclosure
Electrical Internal Frame
Food Packaging
Home Appliances
Hoses
Plastics and Elastomers Functions
Resin
Plastics and Elastomers Processing Methods
Injection Molding
Technical data
Table 1 of 5
5 rows
Characteristic
Value
Unit
Method
Tensile Stress (Break) ¹¹
60
MPa
ASTM D638
Tensile Strain (Break) ¹¹
3.7
%
ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹
8610
MPa
ASTM D638
Flexural Stress ¹¹
110
MPa
ASTM D790
Flexural Modulus ¹¹
7580
MPa
ASTM D790
Table 2 of 5
2 rows
Characteristic
Value
Unit
Method
Density ¹¹
1.57
g/cm³
ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹
0.4
%
ASTM D955
Table 3 of 5
1 row
Characteristic
Value
Unit
Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹