To catalogue
LNP™ THERMOCOMP™ Compound MFB429
- Chemical Family
- PolyolefinsPolypropylenes (PP)
SABIC's Specialties Business LNP™ THERMOCOMP™ MFB429 compound is based on Polypropylene (PP) resin containing 10% glass fiber, 20% glass bead. Added features of this grade include: Flame Retardant.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polypropylene (unspecified)
- Fillers Included
- Glass Bead, Glass Fiber
- Glass Bead
- Glass Fiber
- Additives Included
- Flame Retardant, Mold Release Agent
- Flame Retardant
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые размеры литья, литье крупных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Cost Effective
- Dimensional Stability
- Flame Retardant
- Good Mold Release
- High Stiffness
- Low Warpage
- UL Listed
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Air Cabin Interior
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Covers
- Displays
- Electrical Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 41 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.6 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 5580 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 68 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 4130 | MPa | ASTM D790 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.48 | g/cm³ | ASTM D792 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 130 | °C | ASTM D648 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 267 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 42 | J/m | ASTM D256 |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 225 - 250 | °C |
| Front - Zone 3 Temperature ⁷ | 240 - 250 | °C |
| Middle - Zone 2 Temperature ⁷ | 215 - 225 | °C |
| Rear - Zone 1 Temperature ⁷ | 195 - 205 | °C |
| Mold Temperature ⁷ | 30 - 50 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |