LNP™ THERMOCOMP™ Compound EX11414

Chemical Family: Polyetherimide (PEI)Polyimides (PI)

LNP THERMOCOMP EX11414 compound is based on Polyetherimide (PEI) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive, FAR25.853 Compliant.

Product families

Applications

Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Powertrain & UTH

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Automotive & Transportation — Transportation

Aerospace & Aviation

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyether Imide (PEI)
Fillers Included: Carbon Fiber
Additives Included: Flame Retardant, Mold Release Agent
Flame Retardant
Mold Release Agent
Processing Methods: Injection Molding
Note: ⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
Markets: Automotive & Transportation
Building & Construction
Consumer Goods
Electrical & Electronics
Technology: Plastics
Quality Standards: FAR 25.853
Material Features: Cost Effective
Electrically Conductive
Flame Retardant
Good Mold Release
High Stiffness
High Strength
High Temperature Resistance
Light Weight
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Aerospace Applications
Automotive Applications
Automotive Under The Hood
Building Materials
Construction Applications
Consumer Applications
Electrical Components
Electrical Enclosure
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	230	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.8	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	17380	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	308	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	14600	MPa	ASTM D790

Table 2 of 6

3 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.33	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.23	%	ASTM D570
Poisson's Ratio ¹¹	0.44	—	ASTM E132

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	213	°C	ASTM D648

Table 4 of 6