LNP™ THERMOCOMP™ Compound DF006LXN
- Chemical Family
- Polycarbonate (PC)
LNP THERMOCOMP DF006LXN compound is based on Polycarbonate (PC) resin containing 30% glass fiber. Added features of this grade include: Low Extractables.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 7860.0 - 7860.0 MPa
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовая поддержка литья.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Cost Effective
- Food Contact Acceptable
- High Modulus
- High Stiffness
- Low Extractables
- Low Leachable
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Doors
- Electrical Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 114 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 2.7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 3.2 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 8630 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 149 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 8230 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 114 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 7.5 | % | ISO 527 |
| Flexural Stress ¹¹ | 185 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 7860 | MPa | ISO 178 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.45 | — | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
| Density ¹¹ | 1.45 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.07 | % | ISO 62 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 144 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 140 | °C | ASTM D648 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 145 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 141 | °C | ISO 75/Af |
Table 4 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 914 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 144 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 56 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 14 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 305 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 320 - 330 | °C |
| Middle - Zone 2 Temperature ⁷ | 310 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 295 - 305 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |