LNP™ THERMOCOMP™ Compound AB002

Chemical Family: Acrylonitrile Butadiene Styrene (ABS)Styrenics

LNP THERMOCOMP AB002 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 10% glass bead.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Fillers Included: Glass Bead, Glass Fiber
Glass Bead
Glass Fiber
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Material Features: Cost Effective
Dimensional Stability
Good Mold Release
Low Warpage
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

17 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	34	MPa	ASTM D638
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	35	MPa	ASTM D638
Tensile Strain (Break) ¹¹	3.1	%	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	32	MPa	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2650	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	2.3	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	29	%	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	64	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	63	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2590	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	34	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	30	MPa	ISO 527

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.12	g/cm³	ASTM D792
Density ¹¹	1.11	g/cm³	ISO 1183
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.6 - 0.8	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.7	%	ASTM D955
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.22	%	ASTM D570
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.8 - 1	%	ASTM D955
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.36	%	ISO 62

Table 3 of 5

6 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	93	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	81	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000087	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000089	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	92	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	79	°C	ISO 75/Af

Table 4 of 5