LNP™ THERMOCOMP™ Compound EC006PXQ

Chemical Family: Polyetherimide (PEI)Polyimides (PI)

SABIC's Specialties Business LNP™ THERMOCOMP™ EC006PXQ compound is based on Polyetherimide (PEI) resin containing 30% carbon fiber. Added features of this grade include: Electrically Conductive, Exceptional Processing, FAR25.853 Compliant.

Product families

Applications

Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Powertrain & UTH

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Automotive & Transportation — Transportation

Aerospace & Aviation

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyether Imide (PEI)
Fillers Included: Carbon Fiber
Flexural Modulus: 23060.0 - 23060.0 MPa
Additives Included: Flame Retardant
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Building & Construction
Consumer Goods
Electrical & Electronics
Technology: Plastics
Quality Standards: FAR 25.853
Material Features: Cost Effective
ESD Protection
Electrically Conductive
Flame Retardant
Good Moldability
Good Processability
High Flowability
High Stiffness
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Aerospace Applications
Automotive Applications
Automotive Under The Hood
Building Materials
Construction Applications
Consumer Applications
Electrical Components
Electrical Enclosure
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

13 rows

Characteristic	Value	Unit	Method
Flexural Stress (Break, 2 mm/min) ¹¹	334	MPa	ISO 178
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	272	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.3 - 1.4	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	29520	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	341	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	23800	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	248	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	27560	MPa	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	23060	MPa	ISO 178
Compressive Strength ¹¹	244	MPa	SABIC method
Shear Modulus ¹¹	4726	MPa	ASTM D732

Table 2 of 6

6 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.39	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.11	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.1 - 0.3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.1 - 0.6	%	ASTM D955
Melt Flow Rate (at 380°C, 6.7 kgf) ¹¹	22	g/10 min	ASTM D1238
Poisson's Ratio ¹¹	0.44	—	ASTM E132

Table 3 of 6

3 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	195	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 150°C, flow) ¹¹	0.0000072	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 150°C, xflow) ¹¹	0.000058	1/°C	ASTM E831

Table 4 of 6

1 row

Characteristic	Value	Unit	Method
Surface Resistivity ¹¹	1000	Ω	ASTM D257

Table 5 of 6