LNP™ THERMOCOMP™ Compound LX09404

Chemical Family: Polyether Ether Ketone (PEEK)

SABIC's Specialties Business LNP THERMOCOMP LX09404 compound is based on Polyetheretherketone (PEEK) resin containing 45% carbon fiber. Added features of this grade include: Electrically Conductive, High Modulus This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays
Industrial Automation

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Semiconductor Manufacturing
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyetheretherketone (PEEK)
Fillers Included: Carbon Fiber
Processing Methods: Injection Molding
Note: ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.. ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Consumer Goods
Electrical & Electronics
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Cost Effective
Electrically Conductive
High Stiffness
High Strength
High Temperature Resistance
Light Weight
No Added PFAS
Very Good Heat Resistance
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Cell Phones
Commercial Appliance
Computer Components
Displays
Electrical Components
Electrical Enclosure
Electrical Internal Frame
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	280	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.3	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	41500	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	424	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	29650	MPa	ASTM D790

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.47	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.41	%	ASTM D570

Table 3 of 5

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	332	°C	ASTM D648

Table 4 of 5