LNP™ THERMOCOMP™ Compound KF002L
SABIC's Specialties Business LNP THERMOCOMP KF002L compound is based on POM (Acetal) copolymer resin containing 10% glass fiber. Added features of this grade include: Low Extractables. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Pipes & Plumbing
- Consumer Electronics
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
- Housings & Enclosures
Product Families
- Polyacetals
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyacetal Copolymer (POM)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Material Features
- Cost Effective
- Food Contact Acceptable
- High Impact Resistance
- High Modulus
- High Stiffness
- Low Extractables
- Low Leachable
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Consumer Applications
- Electrical Enclosure
- Electrical Internal Frame
- Food Packaging
- Home Appliances
- Hoses
- Internal Armature
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 66 | MPa | ASTM D638 |
| Tensile Stress (Yield) ¹¹ | 65 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 63 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 63 | MPa | ISO 527 |
| Tensile Strain (Yield) ¹¹ | 2.2 | % | ASTM D638 |
| Tensile Strain (Yield) ¹¹ | 2.1 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 3.2 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 3.4 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 6200 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 103 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 105 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 4820 | MPa | ASTM D790 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.49 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.49 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.2 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.5 - 1.7 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.7 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.6 - 1.8 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.6 | % | ISO 294 |
Table 3 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 162 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 155 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000054 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000605 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000108 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000112 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 162 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 148 | °C | ISO 75/Af |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 384 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 42 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 6 | J | ASTM D3763 |
| Multi-Axial Impact ¹¹ | 2 | J | ISO 6603 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 26 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 200 - 215 | °C |
| Front - Zone 3 Temperature ⁷ | 210 - 220 | °C |
| Middle - Zone 2 Temperature ⁷ | 195 - 205 | °C |
| Rear - Zone 1 Temperature ⁷ | 175 - 190 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |