LNP™ THERMOCOMP™ Compound LF004EX1
- Chemical Family
- Polyether Ether Ketone (PEEK)
SABIC's Specialties Business LNP™ THERMOCOMP™ LF004E1 compound is based on Polyetheretherketone (PEEK) resin containing 20% glass fiber. Added features of this grade include: Easy Molding and Low Warpage
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
- Industrial Automation
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Semiconductor Manufacturing
- Switches & Relays
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyetheretherketone (PEEK)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 7400.0 - 7400.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 5VB
- UL 94 V0
- Technology
- Plastics
- Material Features
- Cost Effective
- Easy To Mold
- Good Moldability
- Good Processability
- High Stiffness
- High Temperature Resistance
- Low Warpage
- Very Good Heat Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- 5G Dipole Antenna
- Air Cabin Interior
- Appliances
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Cooling Fan
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 193 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 7300 | MPa | ASTM D790 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 140 | MPa | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 8800 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.2 | % | ASTM D638 |
| Flexural Strength (at 2 mm/min) ¹¹ | 200 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 7400 | MPa | ISO 178 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 135 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8900 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.1 | % | ISO 527 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.43 | — | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.5 - 0.7 | % | ASTM D955 |
| Density ¹¹ | 1.43 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | max. 0.1 | % | ISO 62 |
Table 3 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 300 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 330 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 305 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 330 | °C | ISO 75/Bf |
| Coefficient of Thermal Expansion (at -40°C to 120°C, flow) ¹¹ | 0.000025 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 120°C, xflow) ¹¹ | 0.000055 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ¹¹ | 130 | °C | UL 746B |
Table 4 of 7
4 rows| Characteristic | Value | Method |
|---|---|---|
| Dielectric Constant (at 1.1 GHz) ¹¹ | 3.48 | SABIC method |
| Dissipation Factor (at 1.1 GHz) ¹¹ | 0.0032 | SABIC method |
| Dielectric Constant (at 1.9 GHz) ¹¹ | 3.5 | SABIC method |
| Dissipation Factor (at 1.9 GHz) ¹¹ | 0.0034 | SABIC method |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 70 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 560 | J/m | ASTM D4812 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 36 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 8.1 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 42 | kJ/m² | ISO 179/1eU |
Table 6 of 7
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 3 - 5 | Hrs |
| Nozzle Temperature ⁷ | 380 - 400 | °C |
| Melt Temperature ⁷ | 380 - 400 | °C |
| Front - Zone 3 Temperature ⁷ | 370 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 360 - 370 | °C |
| Rear - Zone 1 Temperature ⁷ | 290 - 300 | °C |
| Mold Temperature ⁷ | 170 - 200 | °C |
| Screw Speed ⁷ | 50 - 100 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) | min. 1.5 | mm | UL 94 |
| UL Recognized (94-5VB Flame Class Rating) | min. 1.5 | mm | UL 94 |