LNP™ THERMOCOMP™ Compound JF003E
- Chemical Family
- Polysulfones
SABIC's Specialties Business LNP THERMOCOMP JF003E compound is based on Polyethersulfone (PES) resin containing 15% glass fiber. Added features of this grade include: Easy Molding. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyethersulfone (PES)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 5330.0 - 5330.0 MPa
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Easy To Mold
- Flame Retardant
- Good Moldability
- Good Processability
- High Modulus
- High Stiffness
- High Temperature Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 101 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 5660 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 174 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 5330 | MPa | ISO 178 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.8 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 107 | MPa | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 5660 | MPa | ASTM D638 |
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 174 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 5680 | MPa | ASTM D790 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.9 | % | ISO 62 |
| Specific Gravity ¹¹ | 1.49 | — | ASTM D792 |
| Density ¹¹ | 1.48 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.45 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.6 - 0.8 | % | ASTM D955 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 218 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 211 | °C | ISO 75/Af |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 218 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 210 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000042 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000047 | 1/°C | ASTM D696 |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 33 | kJ/m² | ISO 180/1U |
| Multi-Axial Impact ¹¹ | 1 | J | ISO 6603 |
| Izod Impact (Notched, at 23°C) ¹¹ | 43 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 500 | J/m | ASTM D4812 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 7 | J | ASTM D3763 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 | % |
| Melt Temperature ⁷ | 355 - 370 | °C |
| Front - Zone 3 Temperature ⁷ | 370 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 360 - 370 | °C |
| Rear - Zone 1 Temperature ⁷ | 345 - 355 | °C |
| Mold Temperature ⁷ | 140 - 150 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 60 - 100 | rpm |