LNP™ THERMOCOMP™ Compound AR002XXH
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
SABIC's Specialties Business LNP THERMOCOMP AR002XXH compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 10% Barium Sulfate. Added features of this grade include: Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Healthcare Packaging
- Housings & Enclosures
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Barium Sulfate, Mineral
- Barium Sulfate
- Mineral
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- High Stiffness
- Metal Detectable
- No Added PFAS
- X-Ray Detectable
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Electrical Enclosure
- Electrical Internal Frame
- Internal Armature
- Medical Devices
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 40 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.6 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2400 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 68 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2560 | MPa | ASTM D790 |
Table 2 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Specific Gravity ¹¹ | 1.12 | ASTM D792 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 78 | °C | ASTM D648 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 269 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 84 | J/m | ASTM D256 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 - 0.1 | % |
| Melt Temperature ⁷ | 260 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 230 - 245 | °C |
| Rear - Zone 1 Temperature ⁷ | 205 - 215 | °C |
| Mold Temperature ⁷ | 70 - 80 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |