LNP™ THERMOCOMP™ Compound DX09309
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP THERMOCOMP DX09309 compound is based on Polycarbonate (PC) resin containing proprietary fillers. Added features of this grade include: High Dielectric Constant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Mineral, Titanium Dioxide
- Mineral
- Titanium Dioxide
- Flexural Modulus
- 2490.0 - 2490.0 MPa
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Excellent Dielectric Properties
- Good Mold Release
- Heat Stabilized
- No Added PFAS
- Unreinforced
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Electrical Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 27 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 4.2 | % | ASTM D638 |
| Flexural Stress ¹¹ | 60 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 2490 | MPa | ASTM D790 |
Table 2 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 2.24 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.65 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.56 | % | SABIC method |
| Melt Volume Rate (at 280°C, 2.16 kg) ¹¹ | 20 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 280°C, 2.16kg) ¹¹ | 15.7 | cm³/10 min | ASTM D1238 |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 103 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 97 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000062 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000064 | 1/°C | ASTM E831 |
Table 4 of 6
2 rows| Characteristic | Value | Method |
|---|---|---|
| Dielectric Constant (at 1.1 GHz) ¹¹ | 8 | SABIC method |
| Dissipation Factor (at 1.1 GHz) ¹¹ | 0.01 | SABIC method |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 68 | J/m | ASTM D256 |
Table 6 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 90 - 110 | °C |
| Drying Time ⁷ | 3 - 5 | Hrs |
| Melt Temperature ⁷ | 280 - 320 | °C |
| Nozzle Temperature ⁷ | 280 - 320 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 280 | °C |
| Mold Temperature ⁷ | 90 - 120 | °C |
| Back Pressure ⁷ | 1 - 5 | MPa |
| Screw Speed ⁷ | 30 - 100 | rpm |