LNP™ THERMOCOMP™ Compound AW00A
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
SABIC's Specialties Business LNP THERMOCOMP AW00A compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing wollastonite. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Mineral, Wollastonite (CaSiO3)
- Mineral
- Wollastonite (CaSiO3)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Dimensional Stability
- High Stiffness
- Low Warpage
- No Added PFAS
- Wear Resistant
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Doors
- Electrical Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 25 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2.1 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3400 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 49 | MPa | ISO 178 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 39 | MPa | ISO 178 |
| Flexural Strain (Break, at 2 mm/min) ¹¹ | 5.9 | % | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 3900 | MPa | ISO 178 |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.5 | % | SABIC method |
| Density ¹¹ | 1.38 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.24 | % | ISO 62-1 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000069 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000093 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 95 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 81 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 15 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 - 0.1 | % |
| Melt Temperature ⁷ | 260 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 230 - 245 | °C |
| Rear - Zone 1 Temperature ⁷ | 205 - 215 | °C |
| Mold Temperature ⁷ | 70 - 80 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |