LNP™ THERMOCOMP™ Compound DX11355
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP™ THERMOCOMP™ DX11355 compound is based on Polycarbonate (PC) resin containing proprietary fillers and available in black color only. Added features of this grade include: Improved Plating Surface and Mechanical Performance suitable for Laser Direct Structuring (LDS) applications, Improved Impact, Non-Brominated, Non-Chlorinated Flame Retardant.
Product families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Talc
- Additives Included
Flame Retardant, Heat Stabilizer, Metal Deactivator, Mold Release Agent, UV Stabilizer; Flame Retardant; Heat Stabilizer; Metal Deactivator; Mold Release Agent; UV Stabilizer
- Processing Methods
- Injection Molding, Laser Sintering (SLS)
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Material Features
- Cost Effective
- Excellent Dielectric Properties
- Flame Retardant
- Good Colorability
- Good Mold Release
- Heat Stabilized
- High Ductility
- High Impact Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Antenna
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 58 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 52 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5.4 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 70 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2600 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 90 | MPa | ASTM D790 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 89 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2400 | MPa | ASTM D790 |
Table 2 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.27 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.01 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.5 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.5 | % | ASTM D955 |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 12 | g/10 min | ASTM D1238 |
Table 3 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 114 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000062 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000067 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Table 4 of 7
2 rows| Characteristic | Value | Method |
|---|---|---|
| Relative Permittivity (1 GHz) ¹¹ | 2.92 | IEC 60250 |
| Dissipation Factor (at at 1 GHz) ¹¹ | 0.007 | IEC 60250 |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 800 | J/m | ASTM D256 |
| Izod Impact (Notched, at -20°C) ¹¹ | 120 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 167 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at -30°C) ¹¹ | 2120 | J/m | ASTM D4812 |
Table 6 of 7
15 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 100 - 110 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 275 - 300 | °C |
| Nozzle Temperature ⁷ | 275 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 260 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 255 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 290 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 60 - 90 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.6 | mm | UL 94 |