LNP™ THERMOCOMP™ Compound AF001H
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
SABIC's Specialties Business LNP THERMOCOMP AF001H compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 5% glass fiber. Added features of this grade include: Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Healthcare Packaging
- Industrial & Transport Packaging
- Housings & Enclosures
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только для целей выбора материала и не должна применяться в качестве спецификации или использоваться для проектирования деталей или пресс-форм.
- Markets
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- High Stiffness
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Electrical Enclosure
- Electrical Internal Frame
- Internal Armature
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 40 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.3 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2750 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 68 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 2730 | MPa | ASTM D790 |
Table 2 of 2
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 - 0.1 | % |
| Melt Temperature ⁷ | 260 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 230 - 245 | °C |
| Rear - Zone 1 Temperature ⁷ | 205 - 215 | °C |
| Mold Temperature ⁷ | 70 - 80 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |