LNP™ THERMOCOMP™ Compound DX06313

Chemical Family: Polycarbonate (PC)

LNP THERMOCOMP DX06313 compound is based on Polycarbonate (PC) resin containing 30% glass fiber. Added features of this grade include: Impact Modified, Thin-Wall Molding.

Product families

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Fillers Included: Glass Fiber
Flexural Modulus: 6650.0 - 6650.0 MPa
Additives Included: Heat Stabilizer, Impact Modifier, Mold Release Agent; Heat Stabilizer; Impact Modifier; Mold Release Agent
Processing Methods: Injection Molding, Thin Wall Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Consumer Goods
Electrical & Electronics
Flame Rating: UL 94 HB
Technology: Plastics
Material Features: Cost Effective
Good Mold Release
Heat Stabilized
High Impact Resistance
High Modulus
High Stiffness
Impact Modified
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Cell Phones
Computer Components
Displays
Electrical Components
Electrical Enclosure
Electrical Internal Frame
Electrical/Electronic Applications
Enclosure
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding
Thin Wall Injection Molding

Technical data

Table 1 of 6

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	99	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3.6	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	7500	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	170	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	7000	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	90	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3.5	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	7420	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	170	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	6650	MPa	ISO 178

Table 2 of 6

8 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.42	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.3 - 0.5	%	SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	4.6	g/10 min	ASTM D1238
Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹	42	g/10 min	ASTM D1238
Density ¹¹	1.42	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	0.4	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.1	%	ISO 62
Melt Volume Rate (at 300°C, 5.0 kg) ¹¹	32	cm³/10 min	ISO 1133

Table 3 of 6

12 rows

Characteristic	Value	Unit	Method
Vicat Softening Temperature (Rate B/50) ¹¹	142	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	142	°C	ASTM D1525
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	136	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000022	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000022	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000068	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000068	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	143	°C	ISO 306
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	136	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Table 4 of 6

7 rows

Characteristic	Value	Unit	Method
Izod Impact (Notched, at -30°C) ¹¹	120	J/m	ASTM D256
Izod Impact (Notched, at 23°C, Natural & Black Colors) ¹¹	190	J/m	ASTM D256
Izod Impact (Notched, at 23°C, Light & White Colors) ¹¹	90	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	24	J	ASTM D3763
Izod Impact (Notched, 80104, at 23°C) ¹¹	16	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	12	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	15	kJ/m²	ISO 179/1eA

Table 5 of 6

14 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	3 - 4	Hrs
Drying Time (Cumulative) ⁷	48	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	315 - 340	°C
Nozzle Temperature ⁷	310 - 330	°C
Front - Zone 3 Temperature ⁷	315 - 340	°C
Middle - Zone 2 Temperature ⁷	305 - 325	°C
Rear - Zone 1 Temperature ⁷	295 - 315	°C
Mold Temperature ⁷	80 - 115	°C
Back Pressure ⁷	0.3 - 0.7	MPa
Screw Speed ⁷	40 - 70	rpm

Table 6 of 6

1 row

Characteristic	Value	Unit	Method
UL Recognized (94HB Flame Class Rating) ᵖ	1.6	mm	UL 94