LNP™ THERMOCOMP™ Compound D351RCC

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP™ THERMOCOMP™ D351RCC compound is based on recycled Polycarbonate (PC) resin containing 30% glass fiber. Added features of this grade include: High Modulus, Low Warpage, Good Ductility, Non-Brominated & Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) Polycarbonate content up to 40%.

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Density: 1425.0 - 1425.0 kg/m³
Polymer Name: Polycarbonate (PC)
Labeling Claims: Bromine-free, Chlorine-free, Contains PCR Resin, Recyclable, Recycled, Sustainable; Bromine-free; Chlorine-free; Contains PCR Resin; Recyclable; Recycled; Sustainable
Fillers Included: Glass Fiber
Additives Included: Flame Retardant, Heat Stabilizer, Mold Release Agent; Flame Retardant; Heat Stabilizer; Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 V0
Technology: Plastics
Material Features: Cost Effective
Flame Retardant
Good Aesthetics
Good Mold Release
Heat Stabilized
High Ductility
High Impact Resistance
High Modulus
Country Availability: Canada
China (Mainland)
Mexico
USA

Technical data

Table 1 of 6

10 rows

Characteristic	Value	Unit	Method
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	195	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	8550	MPa	ASTM D790
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	130	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.4	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	9210	MPa	ASTM D638
Flexural Strength (at 2 mm/min) ¹¹	183	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7810	MPa	ISO 178
Tensile Stress (Break, 5 mm/min) ¹¹	127	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	9400	MPa	ISO 527

Table 2 of 6

6 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.425	g/cm³	ASTM D792
Melt Flow Rate (at 300°C, 2.16 kgf) ¹¹	36	g/10 min	ASTM D1238
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	19	g/10 min	ASTM D1238
Melt Volume Rate (at 300°C, 2.16 kg) ¹¹	31	cm³/10 min	ISO 1133
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.1 - 0.3	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.1 - 0.3	%	ASTM D955

Table 3 of 6

9 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	113	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	118	°C	ASTM D648
Vicat Softening Temperature (Rate B/50) ¹¹	122	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	126	°C	ISO 306
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.00002	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000068	1/°C	ASTM E831
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Table 4 of 6

4 rows

Characteristic	Value	Unit	Method
Izod Impact (Notched, at 23°C) ¹¹	130	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	465	J/m	ASTM D4812
Izod Impact (Notched, 80104, at 23°C) ¹¹	13	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	31	kJ/m²	ISO 180/1U

Table 5 of 6

11 rows

Characteristic	Value	Unit
Drying Temperature ⁷	110	°C
Drying Time ⁷	3 - 6	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	285 - 310	°C
Nozzle Temperature ⁷	285 - 305	°C
Front - Zone 3 Temperature ⁷	280 - 300	°C
Middle - Zone 2 Temperature ⁷	270 - 290	°C
Rear - Zone 1 Temperature ⁷	260 - 280	°C
Mold Temperature ⁷	80 - 110	°C
Back Pressure ⁷	0.1 - 0.3	MPa
Screw Speed ⁷	50 - 90	rpm

Table 6 of 6

1 row

Characteristic	Value	Unit	Method
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 0.8	mm	UL 94