LNP™ THERMOCOMP™ Compound RX10405H

Chemical Family: Polyamides

SABIC's Specialties Business LNP THERMOCOMP RX10405H compound is based on Nylon 6/6 resin containing 40% carbon fiber. Added features of this grade include: Electrically Conductive, Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies
Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging
Industrial & Transport Packaging

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Carbon Fiber
Processing Methods: Injection Molding
Note: ⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
Markets: Electrical & Electronics
Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Cost Effective
Electrically Conductive
High Stiffness
High Strength
Light Weight
No Added PFAS
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Electrical Enclosure
Electrical Internal Frame
Internal Armature
Medical Devices
Medical Packaging
Medical/Healthcare Applications
Pharmaceutical Packaging
Surgical Devices
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	276	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.6	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	31000	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	386	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	24400	MPa	ASTM D790

Table 2 of 6

1 row

Characteristic	Value	Method
Specific Gravity ¹¹	1.33	ASTM D792

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	256	°C	ASTM D648

Table 4 of 6

1 row

Characteristic	Value	Unit	Method
Surface Resistivity ¹¹	100	Ω	ASTM D257

Table 5 of 6

1 row

Characteristic	Value	Unit	Method
Izod Impact (Notched, at 23°C) ¹¹	101	J/m	ASTM D256

Table 6 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	80	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.15 - 0.25	%
Melt Temperature ⁷	280 - 305	°C
Front - Zone 3 Temperature ⁷	295 - 305	°C
Middle - Zone 2 Temperature ⁷	280 - 295	°C
Rear - Zone 1 Temperature ⁷	265 - 275	°C
Mold Temperature ⁷	95 - 110	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 60	rpm

Product families

Applications

Product Families

Other characteristics

Technical data

Table 1 of 6

Table 2 of 6

Table 3 of 6

Table 4 of 6

Table 5 of 6

Table 6 of 6

More products by SABIC's Specialties Business