LNP™ THERMOCOMP™ Compound OF008A
- Chemical Family
- Polyphenylene Sulfide (PPS)
SABIC's Specialties Business LNP THERMOCOMP OF008A compound is based on branched Polyphenylene Sulfide (PPS) resin containing 40% glass fiber. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ¹⁷ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 5VA
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- High Modulus
- High Stiffness
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
20 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 160 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 182 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 178 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 160 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 178 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.7 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.2 | % | ISO 527 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1.7 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 1.7 | % | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 1.2 | % | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 271 | MPa | ISO 178 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 248 | MPa | ASTM D790 |
Table 2 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.15 - 0.25 | % | SABIC method |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.4 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.8 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.8 - 1.2 | % | ISO 294 |
| Density ¹¹ | 1.65 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.68 | g/cm³ | ASTM D792 |
| Wear Factor Washer ¹¹ | 240 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.41 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.87 | — | ASTM D3702 Modified: Manual |
Table 3 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000026 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 272 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 220 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 200 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 220 | °C | UL 746B |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 261 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000026 | 1/°C | ISO 11359-2 |
Table 4 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Arc Resistance (Tungsten, PLC) ¹⁷ | 5 | PLC Code | ASTM D495 |
| Comparative Tracking Index (UL, PLC) ¹⁷ | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹⁷ | 2 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 4) ¹⁷ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹⁷ | 1 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 0) ¹⁷ | min. 6 | mm | UL 746A |
| Hot Wire Ignition (PLC 1) ¹⁷ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹⁷ | min. 1.5 | mm | UL 746A |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 21 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 587 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 101 | J/m | ASTM D256 |
Table 6 of 7
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 315 - 320 | °C |
| Front - Zone 3 Temperature ⁷ | 330 - 345 | °C |
| Middle - Zone 2 Temperature ⁷ | 320 - 330 | °C |
| Rear - Zone 1 Temperature ⁷ | 305 - 315 | °C |
| Mold Temperature ⁷ | 140 - 165 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.45 | mm | UL 94 |