LNP™ THERMOCOMP™ Compound 9X10401H
SABIC's Specialties Business LNP THERMOCOMP 9X10401H compound is based on Polyphenylsulfone (PPSU) containing proprietary fillers. Added features of this grade include: Healthcare, X-Ray Opaque. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Healthcare Packaging
- Industrial & Transport Packaging
- Housings & Enclosures
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyphenylsulfone (PPSU)
- Fillers Included
- Mineral
- Flexural Modulus
- 2570.0 - 2570.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Metal Detectable
- No Added PFAS
- Unreinforced
- X-Ray Detectable
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Electrical Enclosure
- Electrical Internal Frame
- Internal Armature
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 72 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 57 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 12 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2660 | MPa | ASTM D638 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2720 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 7.10E+01 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 57 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 7 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 12 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2550 | MPa | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2570 | MPa | ISO 178 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.46 | — | ASTM D792 |
| Density ¹¹ | 1.45 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.26 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.8 - 1 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.47 | % | ISO 62 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 214 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 203 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000053 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000053 | 1/°C | ASTM D696 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 213 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 200 | °C | ISO 75/Af |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1640 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 86 | J/m | ASTM D256 |
| Multi-Axial Impact ¹¹ | 29 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 34 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 175 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 2.5 | Hrs |
| Front - Zone 3 Temperature ⁷ | 350 | °C |
| Maximum Moisture Content ⁷ | 0.05 | % |
| Melt Temperature ⁷ | 340 - 390 | °C |
| Middle - Zone 2 Temperature ⁷ | 350 | °C |
| Mold Temperature ⁷ | 140 - 160 | °C |
| Rear - Zone 1 Temperature ⁷ | 320 | °C |