LNP™ THERMOCOMP™ Compound PCAF04FRHH
SABIC's Specialties Business LNP THERMOCOMP PCA04FRHH compound is based on Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 20 % glass fiber. Added features of this grade include: Non-Brominated, Non-Chlorinated Flame Retardants.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Density
- 1320.0 - 1320.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 5800.0 - 5800.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Mold Release Agent
- Material Features
- Cost Effective
- Flame Retardant
- Good Mold Release
- Heat Stabilized
- High Modulus
- High Stiffness
- Non-brominated
- Non-chlorinated
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 85 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 6.20E+03 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 130 | MPa | ISO 178 |
| Flexural Strain (Break, at 2 mm/min) ¹¹ | 2.5 | % | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 5800 | MPa | ISO 178 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Mold Shrinkage (xflow) ᵍ ¹¹ | 0.3 - 0.5 | % | SABIC method |
| Density ¹¹ | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 260°C, 5.0 kg) ¹¹ | 8 | cm³/10 min | ISO 1133 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/120) ¹¹ | 130 | °C | ISO 306 |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 118 | °C | ISO 75/Ae |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Table 4 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL, PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Comparative Tracking Index ʳ ¹¹ | 150 | V | IEC 60112 |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 23 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 90 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 230 - 270 | °C |
| Nozzle Temperature ⁷ | 220 - 260 | °C |
| Front - Zone 3 Temperature ⁷ | 230 - 270 | °C |
| Middle - Zone 2 Temperature ⁷ | 220 - 260 | °C |
| Rear - Zone 1 Temperature ⁷ | 200 - 230 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 50 - 70 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ᵖ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (at 2 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |